Aluminum Nitride vs. Carbon-carbon
Both aluminum nitride and carbon-carbon are non-oxide engineering ceramics. There are 12 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is aluminum nitride and the bottom bar is carbon-carbon.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 2100 | |
| 240 |
| Elastic (Young's, Tensile) Modulus, GPa | 330 | |
| 95 |
| Poisson's Ratio | 0.21 to 0.31 | |
| 0.32 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 1380 | |
| 2400 |
| Specific Heat Capacity, J/kg-K | 780 | |
| 760 |
| Thermal Conductivity, W/m-K | 80 to 190 | |
| 40 |
| Thermal Expansion, µm/m-K | 4.2 to 5.4 | |
| 4.0 |
Electrical Properties
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 10 to 12 | |
| -5.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.9 to 3.3 | |
| 1.7 |
Common Calculations
| Stiffness to Weight: Axial, points | 55 to 63 | |
| 31 |
| Stiffness to Weight: Bending, points | 69 to 80 | |
| 89 |
| Thermal Diffusivity, mm2/s | 31 to 74 | |
| 31 |