Aluminum Nitride vs. PEEK
Aluminum nitride and PEEK belong to fundamentally different material chemistries. Aluminum nitride is a ceramic material, while PEEK is polymeric. Therefore, their performance will be even more dissimilar than would be suggested by the difference in properties. There are 12 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is aluminum nitride and the bottom bar is PEEK.
Mechanical Properties
Compressive (Crushing) Strength, MPa | 2100 | |
120 to 300 |
Elastic (Young's, Tensile) Modulus, GPa | 330 | |
4.0 to 24 |
Flexural Strength, MPa | 190 to 400 | |
150 to 330 |
Thermal Properties
Maximum Temperature: Mechanical, °C | 1380 | |
330 |
Specific Heat Capacity, J/kg-K | 780 | |
1390 to 1700 |
Thermal Conductivity, W/m-K | 80 to 190 | |
0.25 to 0.93 |
Thermal Expansion, µm/m-K | 4.2 to 5.4 | |
15 to 52 |
Electrical Properties
Electrical Resistivity Order of Magnitude, 10x Ω-m | 10 to 12 | |
3.0 to 14 |
Otherwise Unclassified Properties
Density, g/cm3 | 2.9 to 3.3 | |
1.3 to 1.5 |
Common Calculations
Stiffness to Weight: Axial, points | 55 to 63 | |
1.5 to 10 |
Stiffness to Weight: Bending, points | 69 to 80 | |
36 to 73 |
Thermal Diffusivity, mm2/s | 31 to 74 | |
0.1 to 0.51 |