Aluminum Titanate vs. Ferrite
Both aluminum titanate and ferrite are oxide-based engineering ceramics. There are 8 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is aluminum titanate and the bottom bar is ferrite.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 3.2 | |
| 4.7 to 4.8 |
| Elastic (Young's, Tensile) Modulus, GPa | 13 | |
| 120 to 140 |
| Flexural Strength, MPa | 29 | |
| 120 to 150 |
| Fracture Toughness, MPa-m1/2 | 1.0 | |
| 1.4 to 1.5 |
| Stiffness to Weight: Axial, points | 2.2 | |
| 15 to 16 |
| Stiffness to Weight: Bending, points | 24 | |
| 35 to 36 |
| Thermal Conductivity, W/m-K | 1.6 | |
| 3.9 to 6.3 |
| Thermal Expansion, µm/m-K | 2.9 | |
| 8.0 to 9.3 |