Annealed AISI 204 vs. Annealed 88-silver 12-tin-oxide
Annealed AISI 204 belongs to the iron alloys classification, while annealed 88-silver 12-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (28, in this case) are not shown.
For each property being compared, the top bar is annealed AISI 204 and the bottom bar is annealed 88-silver 12-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 86 |
| Elongation at Break, % | 39 | |
| 37 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 240 | |
| 70 |
| Shear Strength, MPa | 500 | |
| 150 |
| Tensile Strength: Ultimate (UTS), MPa | 730 | |
| 230 |
| Tensile Strength: Yield (Proof), MPa | 380 | |
| 110 |