Annealed 70Ag-30Ni Alloy vs. Rolled And Annealed Type 2 Pewter
Both annealed 70Ag-30Ni alloy and rolled and annealed Type 2 pewter are otherwise unclassified metals. Both are furnished in the annealed condition. There are 15 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is annealed 70Ag-30Ni alloy and the bottom bar is rolled and annealed Type 2 pewter.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 52 |
| Poisson's Ratio | 0.35 | |
| 0.35 |
| Shear Modulus, GPa | 39 | |
| 19 |
| Tensile Strength: Ultimate (UTS), MPa | 320 | |
| 59 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 69 |
| Melting Completion (Liquidus), °C | 960 | |
| 300 |
| Melting Onset (Solidus), °C | 960 | |
| 240 |
| Specific Heat Capacity, J/kg-K | 300 | |
| 220 |
| Thermal Expansion, µm/m-K | 17 | |
| 21 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 7.3 |
Common Calculations
| Stiffness to Weight: Axial, points | 5.8 | |
| 3.9 |
| Stiffness to Weight: Bending, points | 16 | |
| 17 |
| Strength to Weight: Axial, points | 8.8 | |
| 2.3 |
| Strength to Weight: Bending, points | 10 | |
| 4.6 |
| Thermal Shock Resistance, points | 13 | |
| 3.9 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Antimony (Sb), % | 0 | |
| 5.0 to 7.5 |
| Arsenic (As), % | 0 | |
| 0 to 0.050 |
| Copper (Cu), % | 0 | |
| 1.5 to 3.0 |
| Iron (Fe), % | 0 | |
| 0 to 0.015 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Nickel (Ni), % | 28.8 to 31 | |
| 0 |
| Silver (Ag), % | 69 to 71 | |
| 0 |
| Tin (Sn), % | 0 | |
| 90 to 93 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0050 |
| Residuals, % | 0 to 0.2 | |
| 0 |