Annealed 80-silver 20-cadmium-oxide vs. Annealed ASTM B617
Both annealed 80-silver 20-cadmium-oxide and annealed ASTM B617 are otherwise unclassified metals. Both are furnished in the annealed condition. There are 8 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is annealed 80-silver 20-cadmium-oxide and the bottom bar is annealed ASTM B617.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 9.9 | |
| 10 |
| Electrical Conductivity: Equal Volume, % IACS | 77 | |
| 83 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 70 | |
| 72 |
| Elongation at Break, % | 15 | |
| 22 |
| Shear Strength, MPa | 190 | |
| 180 |
| Strength to Weight: Axial, points | 8.8 | |
| 7.7 |
| Strength to Weight: Bending, points | 10 | |
| 9.3 |
| Tensile Strength: Ultimate (UTS), MPa | 310 | |
| 290 |