Annealed 85-silver 15-nickel vs. Annealed ASTM B685 Alloy
Both annealed 85-silver 15-nickel and annealed ASTM B685 alloy are otherwise unclassified metals. Both are furnished in the annealed condition. There are 17 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is annealed 85-silver 15-nickel and the bottom bar is annealed ASTM B685 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 88 | |
| 120 |
| Poisson's Ratio | 0.36 | |
| 0.37 |
| Shear Modulus, GPa | 32 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 260 | |
| 660 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 180 |
| Melting Completion (Liquidus), °C | 870 | |
| 1230 |
| Melting Onset (Solidus), °C | 960 | |
| 1200 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 300 |
| Thermal Expansion, µm/m-K | 18 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 86 | |
| 5.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 75 | |
| 4.1 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 11 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.8 | |
| 6.1 |
| Stiffness to Weight: Bending, points | 14 | |
| 15 |
| Strength to Weight: Axial, points | 7.1 | |
| 17 |
| Strength to Weight: Bending, points | 8.9 | |
| 16 |
| Thermal Shock Resistance, points | 12 | |
| 28 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.050 |
| Copper (Cu), % | 0 | |
| 39.5 to 40.5 |
| Iron (Fe), % | 0 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 | |
| 0 to 0.030 |
| Nickel (Ni), % | 13.8 to 16 | |
| 0 |
| Palladium (Pd), % | 0 | |
| 59 to 60.5 |
| Silver (Ag), % | 84 to 86 | |
| 0 to 0.1 |
| Zinc (Zn), % | 0 | |
| 0 to 0.060 |
| Residuals, % | 0 to 0.2 | |
| 0 to 0.2 |