Annealed 88-silver 12-tin-oxide vs. Annealed 350 Maraging Steel
Annealed 88-silver 12-tin-oxide belongs to the otherwise unclassified metals classification, while annealed 350 maraging steel belongs to the iron alloys. There are 5 material properties with values for both materials. Properties with values for just one material (23, in this case) are not shown.
For each property being compared, the top bar is annealed 88-silver 12-tin-oxide and the bottom bar is annealed 350 maraging steel.
Metric UnitsUS Customary Units
Material Properties
| Elongation at Break, % | 37 | |
| 18 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 70 | |
| 190 |
| Shear Strength, MPa | 150 | |
| 710 |
| Tensile Strength: Ultimate (UTS), MPa | 230 | |
| 1140 |
| Tensile Strength: Yield (Proof), MPa | 110 | |
| 830 |