Annealed 88-silver 12-tin-oxide vs. ISO-WD21150-O
Annealed 88-silver 12-tin-oxide belongs to the otherwise unclassified metals classification, while ISO-WD21150-O belongs to the magnesium alloys. There are 6 material properties with values for both materials. Properties with values for just one material (24, in this case) are not shown.
For each property being compared, the top bar is annealed 88-silver 12-tin-oxide and the bottom bar is ISO-WD21150-O.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 86 | |
| 19 |
| Elongation at Break, % | 37 | |
| 11 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 70 | |
| 23 |
| Shear Strength, MPa | 150 | |
| 150 |
| Tensile Strength: Ultimate (UTS), MPa | 230 | |
| 240 |
| Tensile Strength: Yield (Proof), MPa | 110 | |
| 120 |