Annealed 90-platinum 10-iridium vs. Annealed ASTM B541
Both annealed 90-platinum 10-iridium and annealed ASTM B541 are otherwise unclassified metals. Both are furnished in the annealed condition. There are 16 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is annealed 90-platinum 10-iridium and the bottom bar is annealed ASTM B541.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 110 |
| Elongation at Break, % | 34 | |
| 14 |
| Poisson's Ratio | 0.38 | |
| 0.4 |
| Shear Modulus, GPa | 74 | |
| 38 |
| Shear Strength, MPa | 220 | |
| 410 |
| Tensile Strength: Ultimate (UTS), MPa | 330 | |
| 670 |
Thermal Properties
| Latent Heat of Fusion, J/g | 100 | |
| 90 |
| Melting Completion (Liquidus), °C | 1830 | |
| 1110 |
| Specific Heat Capacity, J/kg-K | 130 | |
| 170 |
| Thermal Expansion, µm/m-K | 8.6 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 22 | |
| 17 |
Common Calculations
| Stiffness to Weight: Axial, points | 5.3 | |
| 3.4 |
| Stiffness to Weight: Bending, points | 9.1 | |
| 9.0 |
| Strength to Weight: Axial, points | 4.2 | |
| 11 |
| Strength to Weight: Bending, points | 4.9 | |
| 9.8 |
| Thermal Shock Resistance, points | 13 | |
| 36 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 0 | |
| 13.5 to 15.5 |
| Gold (Au), % | 0 | |
| 70.5 to 72.5 |
| Iridium (Ir), % | 9.5 to 10.5 | |
| 0 |
| Platinum (Pt), % | 89.3 to 90.5 | |
| 8.0 to 9.0 |
| Silver (Ag), % | 0 | |
| 4.0 to 5.0 |
| Zinc (Zn), % | 0 | |
| 0.7 to 1.3 |
| Residuals, % | 0 to 0.2 | |
| 0 to 0.4 |