Annealed Alloy 360 vs. Annealed ASTM B596
Annealed alloy 360 belongs to the nickel alloys classification, while annealed ASTM B596 belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is annealed alloy 360 and the bottom bar is annealed ASTM B596.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 100 |
| Elongation at Break, % | 30 | |
| 17 |
| Poisson's Ratio | 0.3 | |
| 0.41 |
| Shear Modulus, GPa | 77 | |
| 36 |
| Shear Strength, MPa | 510 | |
| 280 |
| Tensile Strength: Ultimate (UTS), MPa | 780 | |
| 450 |
Thermal Properties
| Melting Completion (Liquidus), °C | 1330 | |
| 1060 |
| Melting Onset (Solidus), °C | 1200 | |
| 930 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 150 |
| Thermal Expansion, µm/m-K | 14 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 5.0 | |
| 14 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 5.4 | |
| 6.7 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.3 | |
| 18 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 3.1 |
| Stiffness to Weight: Bending, points | 24 | |
| 8.5 |
| Strength to Weight: Axial, points | 26 | |
| 6.8 |
| Strength to Weight: Bending, points | 23 | |
| 7.1 |
| Thermal Shock Resistance, points | 19 | |
| 22 |