Annealed ASTM B522 Class II vs. Annealed Nickel 201
Annealed ASTM B522 class II belongs to the otherwise unclassified metals classification, while annealed nickel 201 belongs to the nickel alloys. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is annealed ASTM B522 class II and the bottom bar is annealed nickel 201.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 96 | |
| 180 |
| Elongation at Break, % | 28 | |
| 43 |
| Poisson's Ratio | 0.41 | |
| 0.31 |
| Shear Modulus, GPa | 34 | |
| 70 |
| Shear Strength, MPa | 180 | |
| 270 |
| Tensile Strength: Ultimate (UTS), MPa | 280 | |
| 400 |
| Tensile Strength: Yield (Proof), MPa | 120 | |
| 93 |
Thermal Properties
| Latent Heat of Fusion, J/g | 77 | |
| 290 |
| Melting Completion (Liquidus), °C | 1030 | |
| 1450 |
| Melting Onset (Solidus), °C | 1030 | |
| 1440 |
| Specific Heat Capacity, J/kg-K | 160 | |
| 440 |
| Thermal Expansion, µm/m-K | 15 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 11 | |
| 19 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 5.7 | |
| 19 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 8.9 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 63 | |
| 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 75 | |
| 24 |
| Stiffness to Weight: Axial, points | 3.1 | |
| 11 |
| Stiffness to Weight: Bending, points | 8.9 | |
| 21 |
| Strength to Weight: Axial, points | 4.4 | |
| 12 |
| Strength to Weight: Bending, points | 5.5 | |
| 13 |
| Thermal Shock Resistance, points | 13 | |
| 12 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0 | |
| 0 to 0.020 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Gold (Au), % | 68.5 to 69.5 | |
| 0 |
| Iron (Fe), % | 0 | |
| 0 to 0.4 |
| Manganese (Mn), % | 0 | |
| 0 to 0.35 |
| Nickel (Ni), % | 0 | |
| 99 to 100 |
| Platinum (Pt), % | 5.5 to 6.5 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.35 |
| Silver (Ag), % | 24.5 to 25.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.010 |
| Residuals, % | 0 to 0.26 | |
| 0 |