Annealed ASTM B628 vs. Annealed K93600
Annealed ASTM B628 belongs to the otherwise unclassified metals classification, while annealed K93600 belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is annealed ASTM B628 and the bottom bar is annealed K93600.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 83 | |
| 140 |
| Elongation at Break, % | 17 | |
| 35 |
| Shear Strength, MPa | 210 | |
| 320 |
| Tensile Strength: Ultimate (UTS), MPa | 350 | |
| 480 |
Thermal Properties
| Melting Onset (Solidus), °C | 780 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 280 | |
| 520 |
| Thermal Expansion, µm/m-K | 19 | |
| 7.3 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 84 | |
| 2.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 75 | |
| 2.4 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 8.1 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.6 | |
| 9.4 |
| Stiffness to Weight: Bending, points | 14 | |
| 21 |
| Strength to Weight: Axial, points | 9.5 | |
| 16 |
| Strength to Weight: Bending, points | 11 | |
| 17 |
| Thermal Shock Resistance, points | 16 | |
| 34 |