Annealed Palladium vs. Annealed K94200
Annealed palladium belongs to the otherwise unclassified metals classification, while annealed K94200 belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is annealed palladium and the bottom bar is annealed K94200.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 140 |
| Elongation at Break, % | 11 | |
| 32 |
| Poisson's Ratio | 0.39 | |
| 0.34 |
| Shear Modulus, GPa | 43 | |
| 54 |
| Shear Strength, MPa | 120 | |
| 330 |
| Tensile Strength: Ultimate (UTS), MPa | 200 | |
| 500 |
Thermal Properties
| Melting Onset (Solidus), °C | 1550 | |
| 1440 |
| Specific Heat Capacity, J/kg-K | 240 | |
| 500 |
| Thermal Expansion, µm/m-K | 12 | |
| 5.0 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 16 | |
| 2.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 12 | |
| 3.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 12 | |
| 8.2 |
Common Calculations
| Stiffness to Weight: Axial, points | 5.6 | |
| 9.8 |
| Stiffness to Weight: Bending, points | 14 | |
| 21 |
| Strength to Weight: Axial, points | 4.5 | |
| 17 |
| Strength to Weight: Bending, points | 6.2 | |
| 17 |
| Thermal Shock Resistance, points | 9.8 | |
| 49 |