Annealed SAE-AISI D7 vs. Annealed Grade 18 Titanium
Annealed SAE-AISI D7 belongs to the iron alloys classification, while annealed grade 18 titanium belongs to the titanium alloys. There are 20 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is annealed SAE-AISI D7 and the bottom bar is annealed grade 18 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Poisson's Ratio | 0.28 | |
| 0.32 |
| Shear Modulus, GPa | 73 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 800 | |
| 710 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 410 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1640 |
| Melting Onset (Solidus), °C | 1400 | |
| 1590 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 550 |
| Thermal Conductivity, W/m-K | 27 | |
| 8.3 |
| Thermal Expansion, µm/m-K | 11 | |
| 9.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.6 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 11 | |
| 41 |
| Embodied Energy, MJ/kg | 180 | |
| 670 |
| Embodied Water, L/kg | 130 | |
| 270 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 35 |
| Strength to Weight: Axial, points | 29 | |
| 44 |
| Strength to Weight: Bending, points | 25 | |
| 39 |
| Thermal Diffusivity, mm2/s | 7.4 | |
| 3.4 |
| Thermal Shock Resistance, points | 27 | |
| 48 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 | |
| 2.5 to 3.5 |
| Carbon (C), % | 2.2 to 2.5 | |
| 0 to 0.080 |
| Chromium (Cr), % | 11.5 to 13.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 76.6 to 81.9 | |
| 0 to 0.25 |
| Manganese (Mn), % | 0 to 0.6 | |
| 0 |
| Molybdenum (Mo), % | 0.7 to 1.2 | |
| 0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.15 |
| Palladium (Pd), % | 0 | |
| 0.040 to 0.080 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0 to 0.6 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 92.5 to 95.5 |
| Vanadium (V), % | 3.8 to 4.4 | |
| 2.0 to 3.0 |
| Residuals, % | 0 | |
| 0 to 0.4 |