Annealed 350 Maraging Steel vs. Annealed K93600
Both annealed 350 maraging steel and annealed K93600 are iron alloys. Both are furnished in the annealed condition. There are 16 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.
For each property being compared, the top bar is annealed 350 maraging steel and the bottom bar is annealed K93600.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 140 |
| Elongation at Break, % | 18 | |
| 35 |
| Shear Strength, MPa | 710 | |
| 320 |
| Tensile Strength: Ultimate (UTS), MPa | 1140 | |
| 480 |
| Tensile Strength: Yield (Proof), MPa | 830 | |
| 280 |
Thermal Properties
| Melting Onset (Solidus), °C | 1420 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 520 |
| Thermal Expansion, µm/m-K | 12 | |
| 7.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.1 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 190 | |
| 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1770 | |
| 280 |
| Stiffness to Weight: Axial, points | 13 | |
| 9.4 |
| Stiffness to Weight: Bending, points | 23 | |
| 21 |
| Strength to Weight: Axial, points | 38 | |
| 16 |
| Strength to Weight: Bending, points | 29 | |
| 17 |
| Thermal Shock Resistance, points | 35 | |
| 34 |