Annealed 350 Maraging Steel vs. Grade 1 Nickel 625
Annealed 350 maraging steel belongs to the iron alloys classification, while grade 1 nickel 625 belongs to the nickel alloys. They have a modest 27% of their average alloy composition in common, which, by itself, doesn't mean much. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is annealed 350 maraging steel and the bottom bar is grade 1 nickel 625.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 18 | |
| 33 |
| Poisson's Ratio | 0.3 | |
| 0.29 |
| Shear Modulus, GPa | 75 | |
| 79 |
| Shear Strength, MPa | 710 | |
| 600 |
| Tensile Strength: Ultimate (UTS), MPa | 1140 | |
| 910 |
| Tensile Strength: Yield (Proof), MPa | 830 | |
| 450 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 330 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1350 |
| Melting Onset (Solidus), °C | 1420 | |
| 1290 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 440 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 39 | |
| 80 |
| Density, g/cm3 | 8.2 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 5.6 | |
| 14 |
| Embodied Energy, MJ/kg | 74 | |
| 190 |
| Embodied Water, L/kg | 160 | |
| 290 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 190 | |
| 250 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1770 | |
| 490 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 23 |
| Strength to Weight: Axial, points | 38 | |
| 29 |
| Strength to Weight: Bending, points | 29 | |
| 24 |
| Thermal Shock Resistance, points | 35 | |
| 25 |
Alloy Composition
| Aluminum (Al), % | 0.050 to 0.15 | |
| 0 to 0.4 |
| Boron (B), % | 0 to 0.0030 | |
| 0 |
| Calcium (Ca), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0 to 0.030 | |
| 0 to 0.1 |
| Chromium (Cr), % | 0 | |
| 20 to 23 |
| Cobalt (Co), % | 11.5 to 12.5 | |
| 0 to 1.0 |
| Iron (Fe), % | 61.2 to 64.6 | |
| 0 to 5.0 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 4.6 to 5.2 | |
| 8.0 to 10 |
| Nickel (Ni), % | 18 to 19 | |
| 58 to 68.9 |
| Niobium (Nb), % | 0 | |
| 3.2 to 4.2 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.015 |
| Titanium (Ti), % | 1.3 to 1.6 | |
| 0 to 0.4 |
| Zirconium (Zr), % | 0 to 0.020 | |
| 0 |