Annealed R31538 Cobalt vs. Annealed SAE-AISI M52
Annealed R31538 cobalt belongs to the cobalt alloys classification, while annealed SAE-AISI M52 belongs to the iron alloys. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is annealed R31538 cobalt and the bottom bar is annealed SAE-AISI M52.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 86 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 1020 | |
| 710 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 260 |
| Melting Completion (Liquidus), °C | 1360 | |
| 1510 |
| Melting Onset (Solidus), °C | 1290 | |
| 1470 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 460 |
| Thermal Conductivity, W/m-K | 13 | |
| 31 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.0 | |
| 8.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.1 | |
| 10 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.4 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 8.1 | |
| 7.5 |
| Embodied Energy, MJ/kg | 110 | |
| 110 |
| Embodied Water, L/kg | 530 | |
| 89 |
Common Calculations
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 34 | |
| 25 |
| Strength to Weight: Bending, points | 27 | |
| 22 |
| Thermal Diffusivity, mm2/s | 3.5 | |
| 8.4 |
| Thermal Shock Resistance, points | 25 | |
| 21 |
Alloy Composition
| Carbon (C), % | 0.15 to 0.35 | |
| 0.85 to 1.0 |
| Chromium (Cr), % | 26 to 30 | |
| 3.5 to 4.3 |
| Cobalt (Co), % | 58.7 to 68.9 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 0.75 | |
| 84.4 to 88.9 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.15 to 0.45 |
| Molybdenum (Mo), % | 5.0 to 7.0 | |
| 4.0 to 4.9 |
| Nickel (Ni), % | 0 to 1.0 | |
| 0 to 0.3 |
| Nitrogen (N), % | 0 to 0.25 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 1.0 | |
| 0.2 to 0.6 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 | |
| 0.75 to 1.5 |
| Vanadium (V), % | 0 | |
| 1.7 to 2.3 |