Annealed K93600 vs. Annealed S17700 Stainless Steel

Both annealed K93600 and annealed S17700 stainless steel are iron alloys. Both are furnished in the annealed condition. There are 22 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is annealed K93600 and the bottom bar is annealed S17700 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130
180
Elastic (Young's, Tensile) Modulus, GPa 140
200
Elongation at Break, % 35
23
Shear Strength, MPa 320
750
Tensile Strength: Ultimate (UTS), MPa 480
1180
Tensile Strength: Yield (Proof), MPa 280
430

Thermal Properties

Maximum Temperature: Mechanical, °C 440
890
Melting Onset (Solidus), °C 1430
1400
Specific Heat Capacity, J/kg-K 520
480
Thermal Conductivity, W/m-K 13
15
Thermal Expansion, µm/m-K 7.3
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.7

Otherwise Unclassified Properties

Density, g/cm3 8.1
7.7

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
210
Resilience: Unit (Modulus of Resilience), kJ/m3 280
460
Stiffness to Weight: Axial, points 9.4
14
Stiffness to Weight: Bending, points 21
25
Strength to Weight: Axial, points 16
42
Strength to Weight: Bending, points 17
32
Thermal Diffusivity, mm2/s 3.1
4.1
Thermal Shock Resistance, points 34
39