Annealed K93600 vs. Rolled And Annealed Type 2 Pewter
Annealed K93600 belongs to the iron alloys classification, while rolled and annealed Type 2 pewter belongs to the otherwise unclassified metals. There are 12 material properties with values for both materials. Properties with values for just one material (20, in this case) are not shown.
For each property being compared, the top bar is annealed K93600 and the bottom bar is rolled and annealed Type 2 pewter.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 130 | |
| 18 |
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 52 |
| Tensile Strength: Ultimate (UTS), MPa | 480 | |
| 59 |
Thermal Properties
| Melting Onset (Solidus), °C | 1430 | |
| 240 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 220 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 21 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 7.3 |
Common Calculations
| Stiffness to Weight: Axial, points | 9.4 | |
| 3.9 |
| Stiffness to Weight: Bending, points | 21 | |
| 17 |
| Strength to Weight: Axial, points | 16 | |
| 2.3 |
| Strength to Weight: Bending, points | 17 | |
| 4.6 |
| Thermal Shock Resistance, points | 34 | |
| 3.9 |