Annealed K93600 vs. Annealed K93500 Alloy
Both annealed K93600 and annealed K93500 alloy are iron alloys. Both are furnished in the annealed condition. There are 14 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.
For each property being compared, the top bar is annealed K93600 and the bottom bar is annealed K93500 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 130 | |
160 |
Elastic (Young's, Tensile) Modulus, GPa | 140 | |
190 |
Tensile Strength: Ultimate (UTS), MPa | 480 | |
490 |
Tensile Strength: Yield (Proof), MPa | 280 | |
290 |
Thermal Properties
Melting Onset (Solidus), °C | 1430 | |
1380 |
Specific Heat Capacity, J/kg-K | 520 | |
460 |
Thermal Expansion, µm/m-K | 7.3 | |
12 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.1 | |
8.2 |
Common Calculations
Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 | |
220 |
Stiffness to Weight: Axial, points | 9.4 | |
13 |
Stiffness to Weight: Bending, points | 21 | |
23 |
Strength to Weight: Axial, points | 16 | |
17 |
Strength to Weight: Bending, points | 17 | |
17 |
Thermal Shock Resistance, points | 34 | |
15 |