Annealed K94200 vs. Annealed K93050 Alloy
Both annealed K94200 and annealed K93050 alloy are iron alloys. Both are furnished in the annealed condition. There are 15 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is annealed K94200 and the bottom bar is annealed K93050 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 140 | |
190 |
Poisson's Ratio | 0.34 | |
0.3 |
Shear Modulus, GPa | 54 | |
72 |
Tensile Strength: Ultimate (UTS), MPa | 500 | |
500 |
Tensile Strength: Yield (Proof), MPa | 270 | |
300 |
Thermal Properties
Melting Onset (Solidus), °C | 1440 | |
1380 |
Specific Heat Capacity, J/kg-K | 500 | |
460 |
Thermal Expansion, µm/m-K | 5.0 | |
12 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.2 | |
8.2 |
Common Calculations
Resilience: Unit (Modulus of Resilience), kJ/m3 | 250 | |
240 |
Stiffness to Weight: Axial, points | 9.8 | |
13 |
Stiffness to Weight: Bending, points | 21 | |
23 |
Strength to Weight: Axial, points | 17 | |
17 |
Strength to Weight: Bending, points | 17 | |
17 |
Thermal Shock Resistance, points | 49 | |
16 |