O61 C63800 Bronze vs. O61 C71640 Copper-nickel
Both O61 C63800 bronze and O61 C71640 copper-nickel are copper alloys. Both are furnished in the O61 (annealed) temper. They have 66% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is O61 C63800 bronze and the bottom bar is O61 C71640 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 140 |
| Poisson's Ratio | 0.34 | |
| 0.33 |
| Shear Modulus, GPa | 43 | |
| 52 |
| Tensile Strength: Ultimate (UTS), MPa | 570 | |
| 490 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 240 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 260 |
| Melting Completion (Liquidus), °C | 1030 | |
| 1180 |
| Melting Onset (Solidus), °C | 1000 | |
| 1120 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 410 |
| Thermal Conductivity, W/m-K | 40 | |
| 29 |
| Thermal Expansion, µm/m-K | 17 | |
| 15 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 10 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 10 | |
| 7.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 40 |
| Density, g/cm3 | 8.6 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 5.0 |
| Embodied Energy, MJ/kg | 45 | |
| 73 |
| Embodied Water, L/kg | 330 | |
| 280 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.4 | |
| 8.7 |
| Stiffness to Weight: Bending, points | 19 | |
| 20 |
| Strength to Weight: Axial, points | 18 | |
| 15 |
| Strength to Weight: Bending, points | 18 | |
| 16 |
| Thermal Diffusivity, mm2/s | 11 | |
| 8.2 |
| Thermal Shock Resistance, points | 20 | |
| 16 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 2.5 to 3.1 | |
| 0 |
| Cobalt (Co), % | 0.25 to 0.55 | |
| 0 |
| Copper (Cu), % | 92.4 to 95.8 | |
| 61.7 to 67.8 |
| Iron (Fe), % | 0 to 0.2 | |
| 1.7 to 2.3 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 0.1 | |
| 1.5 to 2.5 |
| Nickel (Ni), % | 0 to 0.2 | |
| 29 to 32 |
| Silicon (Si), % | 1.5 to 2.1 | |
| 0 |
| Zinc (Zn), % | 0 to 0.8 | |
| 0 to 1.0 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.5 |