Annealed R05200 Tantalum vs. Annealed R60901 Alloy
Both annealed R05200 tantalum and annealed R60901 alloy are otherwise unclassified metals. Both are furnished in the annealed condition. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is annealed R05200 tantalum and the bottom bar is annealed R60901 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 98 |
| Elongation at Break, % | 28 | |
| 22 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 69 | |
| 37 |
| Tensile Strength: Ultimate (UTS), MPa | 210 | |
| 500 |
| Tensile Strength: Yield (Proof), MPa | 140 | |
| 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 250 |
| Melting Completion (Liquidus), °C | 3020 | |
| 1870 |
| Specific Heat Capacity, J/kg-K | 140 | |
| 270 |
| Thermal Conductivity, W/m-K | 59 | |
| 17 |
| Thermal Expansion, µm/m-K | 6.5 | |
| 6.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 6.6 |
| Embodied Water, L/kg | 650 | |
| 270 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 53 | |
| 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 50 | |
| 640 |
| Stiffness to Weight: Axial, points | 6.2 | |
| 8.3 |
| Stiffness to Weight: Bending, points | 11 | |
| 23 |
| Strength to Weight: Axial, points | 3.6 | |
| 21 |
| Strength to Weight: Bending, points | 4.8 | |
| 21 |
| Thermal Diffusivity, mm2/s | 25 | |
| 9.7 |
| Thermal Shock Resistance, points | 13 | |
| 58 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0 to 0.010 | |
| 0 |
| Hydrogen (H), % | 0 to 0.0015 | |
| 0 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 |
| Molybdenum (Mo), % | 0 to 0.020 | |
| 0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Niobium (Nb), % | 0 to 0.1 | |
| 2.4 to 2.8 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 |
| Oxygen (O), % | 0 to 0.015 | |
| 0 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 |
| Tantalum (Ta), % | 99.8 to 100 | |
| 0 |
| Titanium (Ti), % | 0 to 0.010 | |
| 0 |
| Tungsten (W), % | 0 to 0.050 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 96.8 to 97.5 |
| Residuals, % | 0 | |
| 0 to 0.29 |