M20 C61300 Bronze vs. M20 C72500 Copper-nickel
Both M20 C61300 bronze and M20 C72500 copper-nickel are copper alloys. Both are furnished in the M20 (as hot rolled) condition. They have 88% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is M20 C61300 bronze and the bottom bar is M20 C72500 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 43 | |
| 45 |
| Tensile Strength: Ultimate (UTS), MPa | 550 | |
| 420 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 210 |
| Melting Completion (Liquidus), °C | 1050 | |
| 1130 |
| Melting Onset (Solidus), °C | 1040 | |
| 1060 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 390 |
| Thermal Conductivity, W/m-K | 55 | |
| 54 |
| Thermal Expansion, µm/m-K | 18 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 12 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 13 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 35 |
| Density, g/cm3 | 8.5 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 3.6 |
| Embodied Energy, MJ/kg | 49 | |
| 55 |
| Embodied Water, L/kg | 370 | |
| 320 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.5 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 18 | |
| 13 |
| Strength to Weight: Bending, points | 18 | |
| 14 |
| Thermal Diffusivity, mm2/s | 15 | |
| 16 |
| Thermal Shock Resistance, points | 19 | |
| 14 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 6.0 to 7.5 | |
| 0 |
| Copper (Cu), % | 88 to 91.8 | |
| 85.2 to 89.7 |
| Iron (Fe), % | 2.0 to 3.0 | |
| 0 to 0.6 |
| Lead (Pb), % | 0 to 0.010 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 0.2 | |
| 0 to 0.2 |
| Nickel (Ni), % | 0 to 0.15 | |
| 8.5 to 10.5 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 |
| Tin (Sn), % | 0.2 to 0.5 | |
| 1.8 to 2.8 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 to 0.5 |
| Residuals, % | 0 to 0.2 | |
| 0 to 0.2 |