Automotive Grey Cast Iron vs. AWS ERNiCr-3
Automotive grey cast iron belongs to the iron alloys classification, while AWS ERNiCr-3 belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is automotive grey cast iron and the bottom bar is AWS ERNiCr-3.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 190 |
| Elongation at Break, % | 9.6 to 14 | |
| 34 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 69 to 70 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 140 to 290 | |
| 630 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 to 280 | |
| 320 |
| Melting Completion (Liquidus), °C | 1380 to 1390 | |
| 1380 |
| Melting Onset (Solidus), °C | 1340 to 1350 | |
| 1330 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 460 |
| Thermal Expansion, µm/m-K | 12 to 14 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 to 3.0 | |
| 70 |
| Density, g/cm3 | 7.5 to 7.6 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 1.5 to 1.7 | |
| 11 |
| Embodied Energy, MJ/kg | 21 to 24 | |
| 160 |
| Embodied Water, L/kg | 44 to 51 | |
| 280 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 5.2 to 11 | |
| 21 |
| Strength to Weight: Bending, points | 8.0 to 13 | |
| 19 |
| Thermal Shock Resistance, points | 4.2 to 8.6 | |
| 18 |