Automotive Grey Cast Iron vs. Solder Alloy 122
Automotive grey cast iron belongs to the iron alloys classification, while solder alloy 122 belongs to the otherwise unclassified metals. There are 25 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is automotive grey cast iron and the bottom bar is solder alloy 122.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 160 to 280 | |
| 10 |
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 20 |
| Elongation at Break, % | 9.6 to 14 | |
| 30 |
| Poisson's Ratio | 0.29 | |
| 0.43 |
| Shear Modulus, GPa | 69 to 70 | |
| 6.9 |
| Tensile Strength: Ultimate (UTS), MPa | 140 to 290 | |
| 30 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 to 280 | |
| 27 |
| Melting Completion (Liquidus), °C | 1380 to 1390 | |
| 300 |
| Melting Onset (Solidus), °C | 1340 to 1350 | |
| 270 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 140 |
| Thermal Conductivity, W/m-K | 41 to 43 | |
| 25 |
| Thermal Expansion, µm/m-K | 12 to 14 | |
| 28 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 to 7.6 | |
| 8.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.8 to 9.1 | |
| 7.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 to 3.0 | |
| 75 |
| Density, g/cm3 | 7.5 to 7.6 | |
| 11 |
| Embodied Carbon, kg CO2/kg material | 1.5 to 1.7 | |
| 5.0 |
| Embodied Energy, MJ/kg | 21 to 24 | |
| 84 |
| Embodied Water, L/kg | 44 to 51 | |
| 540 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 1.0 |
| Stiffness to Weight: Bending, points | 25 | |
| 8.2 |
| Strength to Weight: Axial, points | 5.2 to 11 | |
| 0.77 |
| Strength to Weight: Bending, points | 8.0 to 13 | |
| 2.0 |
| Thermal Diffusivity, mm2/s | 11 to 12 | |
| 17 |
| Thermal Shock Resistance, points | 4.2 to 8.6 | |
| 3.9 |