Automotive Malleable Cast Iron vs. 85-silver 15-cadmium-oxide
Automotive malleable cast iron belongs to the iron alloys classification, while 85-silver 15-cadmium-oxide belongs to the otherwise unclassified metals. There are 7 material properties with values for both materials. Properties with values for just one material (22, in this case) are not shown.
For each property being compared, the top bar is automotive malleable cast iron and the bottom bar is 85-silver 15-cadmium-oxide.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 7.6 | |
| 10 |
| Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
| 64 to 82 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.7 | |
| 57 to 73 |
| Elongation at Break, % | 1.0 to 10 | |
| 2.2 to 16 |
| Strength to Weight: Axial, points | 13 to 26 | |
| 8.1 to 12 |
| Strength to Weight: Bending, points | 14 to 24 | |
| 9.7 to 13 |
| Tensile Strength: Ultimate (UTS), MPa | 350 to 720 | |
| 290 to 440 |