Automotive Malleable Cast Iron vs. 88-silver 12-tin-oxide
Automotive malleable cast iron belongs to the iron alloys classification, while 88-silver 12-tin-oxide belongs to the otherwise unclassified metals. There are 5 material properties with values for both materials. Properties with values for just one material (24, in this case) are not shown.
For each property being compared, the top bar is automotive malleable cast iron and the bottom bar is 88-silver 12-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
| 84 to 86 |
| Elongation at Break, % | 1.0 to 10 | |
| 9.0 to 37 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 6.8 to 30 | |
| 24 to 70 |
| Tensile Strength: Ultimate (UTS), MPa | 350 to 720 | |
| 230 to 280 |
| Tensile Strength: Yield (Proof), MPa | 220 to 590 | |
| 110 to 260 |