Automotive Malleable Cast Iron vs. EN 1.5521 Steel

Both automotive malleable cast iron and EN 1.5521 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is automotive malleable cast iron and the bottom bar is EN 1.5521 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130 to 290
130 to 180
Elastic (Young's, Tensile) Modulus, GPa 180
190
Elongation at Break, % 1.0 to 10
11 to 21
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 70
73
Tensile Strength: Ultimate (UTS), MPa 350 to 720
430 to 1390
Tensile Strength: Yield (Proof), MPa 220 to 590
300 to 490

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 41
51
Thermal Expansion, µm/m-K 14
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
1.9
Density, g/cm3 7.6
7.8
Embodied Carbon, kg CO2/kg material 1.5
1.4
Embodied Energy, MJ/kg 20
19
Embodied Water, L/kg 45
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 6.8 to 30
44 to 230
Resilience: Unit (Modulus of Resilience), kJ/m3 130 to 950
250 to 630
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 13 to 26
15 to 49
Strength to Weight: Bending, points 14 to 24
16 to 35
Thermal Diffusivity, mm2/s 11
14
Thermal Shock Resistance, points 9.9 to 21
13 to 41

Alloy Composition

Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 2.2 to 2.9
0.16 to 0.2
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 93.6 to 96.7
98 to 98.9
Manganese (Mn), % 0.15 to 1.3
0.9 to 1.2
Phosphorus (P), % 0.020 to 0.15
0 to 0.025
Silicon (Si), % 0.9 to 1.9
0 to 0.3
Sulfur (S), % 0.020 to 0.2
0 to 0.025