Automotive Malleable Cast Iron vs. N08028 Stainless Steel
Both automotive malleable cast iron and N08028 stainless steel are iron alloys. They have a modest 36% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is automotive malleable cast iron and the bottom bar is N08028 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 130 to 290 | |
| 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 200 |
| Elongation at Break, % | 1.0 to 10 | |
| 45 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 70 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 350 to 720 | |
| 570 |
| Tensile Strength: Yield (Proof), MPa | 220 to 590 | |
| 240 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 320 |
| Melting Completion (Liquidus), °C | 1410 | |
| 1420 |
| Melting Onset (Solidus), °C | 1370 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 41 | |
| 12 |
| Thermal Expansion, µm/m-K | 14 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 37 |
| Density, g/cm3 | 7.6 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 6.4 |
| Embodied Energy, MJ/kg | 20 | |
| 89 |
| Embodied Water, L/kg | 45 | |
| 240 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 6.8 to 30 | |
| 210 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 to 950 | |
| 140 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 13 to 26 | |
| 19 |
| Strength to Weight: Bending, points | 14 to 24 | |
| 19 |
| Thermal Diffusivity, mm2/s | 11 | |
| 3.2 |
| Thermal Shock Resistance, points | 9.9 to 21 | |
| 12 |
Alloy Composition
| Carbon (C), % | 2.2 to 2.9 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 | |
| 26 to 28 |
| Copper (Cu), % | 0 | |
| 0.6 to 1.4 |
| Iron (Fe), % | 93.6 to 96.7 | |
| 29 to 40.4 |
| Manganese (Mn), % | 0.15 to 1.3 | |
| 0 to 2.5 |
| Molybdenum (Mo), % | 0 | |
| 3.0 to 4.0 |
| Nickel (Ni), % | 0 | |
| 30 to 34 |
| Phosphorus (P), % | 0.020 to 0.15 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.9 to 1.9 | |
| 0 to 1.0 |
| Sulfur (S), % | 0.020 to 0.2 | |
| 0 to 0.030 |