Boron Carbide vs. Zircon
Boron carbide belongs to the non-oxide engineering ceramics classification, while zircon belongs to the oxide-based engineering ceramics. There are 9 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is boron carbide and the bottom bar is zircon.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 2.1 to 2.7 | |
| 3.9 |
| Dielectric Constant (Relative Permittivity) At 1 MHz | 6.4 | |
| 8.8 |
| Flexural Strength, MPa | 170 to 410 | |
| 450 |
| Maximum Temperature: Mechanical, °C | 1000 to 2500 | |
| 1650 |
| Strength to Weight: Axial, points | 37 to 47 | |
| 21 |
| Strength to Weight: Bending, points | 42 to 53 | |
| 25 |
| Tensile Strength: Ultimate (UTS), MPa | 350 | |
| 290 |
| Thermal Conductivity, W/m-K | 31 to 90 | |
| 3.5 |
| Thermal Expansion, µm/m-K | 4.5 to 5.6 | |
| 5.0 |