Grade BO Boron Nitride vs. Fused Silica
Grade BO boron nitride belongs to the non-oxide engineering ceramics classification, while fused silica belongs to the glass and glass-ceramics. There are 16 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is grade BO boron nitride and the bottom bar is fused silica.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 170 | |
| 1100 |
| Elastic (Young's, Tensile) Modulus, GPa | 60 | |
| 73 |
| Flexural Strength, MPa | 95 | |
| 67 |
| Poisson's Ratio | 0.11 | |
| 0.17 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 1050 | |
| 1080 |
| Specific Heat Capacity, J/kg-K | 1610 | |
| 720 |
| Thermal Conductivity, W/m-K | 30 | |
| 1.4 |
| Thermal Expansion, µm/m-K | 7.5 | |
| 0.5 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 4.4 | |
| 3.8 |
| Dielectric Strength (Breakdown Potential), kV/mm | 61 | |
| 30 |
| Electrical Dissipation At 1 MHz | 0.0011 | |
| 0.00011 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 13 | |
| 14 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.9 | |
| 2.2 |
Common Calculations
| Stiffness to Weight: Axial, points | 18 | |
| 18 |
| Stiffness to Weight: Bending, points | 69 | |
| 63 |
| Thermal Diffusivity, mm2/s | 9.9 | |
| 0.85 |