Carbon-carbon vs. Low Expansion Glass-ceramic
Carbon-carbon belongs to the non-oxide engineering ceramics classification, while low expansion glass-ceramic belongs to the glass and glass-ceramics. There are 15 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is carbon-carbon and the bottom bar is low expansion glass-ceramic.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 95 | |
| 83 |
| Poisson's Ratio | 0.32 | |
| 0.22 |
| Tensile Strength: Ultimate (UTS), MPa | 19 | |
| 53 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 2400 | |
| 690 |
| Specific Heat Capacity, J/kg-K | 760 | |
| 800 |
| Thermal Conductivity, W/m-K | 40 | |
| 1.5 |
| Thermal Expansion, µm/m-K | 4.0 | |
| 1.7 |
Electrical Properties
| Electrical Resistivity Order of Magnitude, 10x Ω-m | -5.0 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.7 | |
| 2.4 |
Common Calculations
| Stiffness to Weight: Axial, points | 31 | |
| 19 |
| Stiffness to Weight: Bending, points | 89 | |
| 59 |
| Strength to Weight: Axial, points | 3.0 | |
| 6.1 |
| Strength to Weight: Bending, points | 9.1 | |
| 13 |
| Thermal Diffusivity, mm2/s | 31 | |
| 0.76 |
| Thermal Shock Resistance, points | 3.5 | |
| 28 |