CAB vs. PLA
Both CAB and PLA are thermoplastics. There are 12 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is CAB and the bottom bar is PLA.
Metric UnitsUS Customary Units
Mechanical Properties
| Elongation at Break, % | 50 to 55 | |
| 6.0 |
| Flexural Modulus, GPa | 0.8 to 1.7 | |
| 4.0 |
| Flexural Strength, MPa | 21 to 57 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 20 to 50 | |
| 50 |
Thermal Properties
| Glass Transition Temperature, °C | 140 | |
| 60 |
| Heat Deflection Temperature At 455 kPa (66 psi), °C | 68 to 92 | |
| 65 |
| Specific Heat Capacity, J/kg-K | 1460 | |
| 1800 |
| Thermal Conductivity, W/m-K | 0.25 | |
| 0.13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.2 | |
| 1.3 |
Common Calculations
| Strength to Weight: Axial, points | 4.8 to 12 | |
| 11 |
| Strength to Weight: Bending, points | 14 to 25 | |
| 24 |
| Thermal Diffusivity, mm2/s | 0.14 to 0.15 | |
| 0.058 |