CAP vs. PTFE

Both CAP and PTFE are thermoplastics. There are 13 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is CAP and the bottom bar is PTFE.

Cellulose Acetate Propionate (CAP)Polytetrafluoroethylene (PTFE)

Metric UnitsUS Customary Units

Mechanical Properties

Elongation at Break, %		35 to 50
Elongation at Break, %		75 to 300

Flexural Modulus, GPa		1.2 to 1.9
Flexural Modulus, GPa		0.4 to 1.3

Flexural Strength, MPa		29 to 56
Flexural Strength, MPa		13 to 50

Tensile Strength: Ultimate (UTS), MPa		28 to 45
Tensile Strength: Ultimate (UTS), MPa		13 to 25

Thermal Properties

Heat Deflection Temperature At 1.82 MPa (264 psi), °C		65 to 80
Heat Deflection Temperature At 1.82 MPa (264 psi), °C		66 to 70

Thermal Conductivity, W/m-K		0.25
Thermal Conductivity, W/m-K		0.24 to 0.65

Thermal Expansion, µm/m-K		14
Thermal Expansion, µm/m-K		110 to 120

Electrical Properties

Dielectric Constant (Relative Permittivity) At 1 MHz		3.6
Dielectric Constant (Relative Permittivity) At 1 MHz		2.1 to 2.4

Electrical Resistivity Order of Magnitude, 10^x Ω-m		16
Electrical Resistivity Order of Magnitude, 10^x Ω-m		2.0 to 18

Otherwise Unclassified Properties

Density, g/cm³		1.2
Density, g/cm³		2.1 to 2.3

Water Absorption After 24 Hours, %		1.4 to 1.7
Water Absorption After 24 Hours, %		0.0093 to 0.050

Common Calculations

Strength to Weight: Axial, points		6.5 to 10
Strength to Weight: Axial, points		1.7 to 3.2

Strength to Weight: Bending, points		17 to 23
Strength to Weight: Bending, points		5.7 to 8.7