Ceria vs. Ferrite

Both ceria and ferrite are oxide-based engineering ceramics. There are 8 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is ceria and the bottom bar is ferrite.

Metric UnitsUS Customary Units

Material Properties

Compressive (Crushing) Strength, MPa 590
430 to 2000
Density, g/cm3 7.6
4.7 to 4.8
Elastic (Young's, Tensile) Modulus, GPa 180
120 to 140
Electrical Resistivity Order of Magnitude, 10x Ω-m 4.0
1.0 to 1.5
Specific Heat Capacity, J/kg-K 390
710 to 1050
Stiffness to Weight: Axial, points 13
15 to 16
Stiffness to Weight: Bending, points 25
35 to 36
Thermal Expansion, µm/m-K 11
8.0 to 9.3