Cesium Iodide vs. Gallium Arsenide
Both cesium iodide and gallium arsenide are non-glass optical ceramics. There are 13 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is cesium iodide and the bottom bar is gallium arsenide.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 4.0 | |
| 85 |
| Knoop Hardness | 20 | |
| 750 |
| Poisson's Ratio | 0.21 | |
| 0.31 |
Thermal Properties
| Melting Onset (Solidus), °C | 620 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 200 | |
| 360 |
| Thermal Conductivity, W/m-K | 1.1 | |
| 47 |
| Thermal Expansion, µm/m-K | 48 | |
| 5.6 |
Otherwise Unclassified Properties
| Density, g/cm3 | 4.5 | |
| 5.3 |
| Light Transmission Range, µm | 0.25 to 55 | |
| 1.0 to 16 |
| Refractive Index | 1.9 | |
| 3.4 |
Common Calculations
| Stiffness to Weight: Axial, points | 0.49 | |
| 8.9 |
| Stiffness to Weight: Bending, points | 12 | |
| 28 |
| Thermal Diffusivity, mm2/s | 1.2 | |
| 25 |