Chromium 33 vs. Grade 36 Titanium
Chromium 33 belongs to the otherwise unclassified metals classification, while grade 36 titanium belongs to the titanium alloys. There are 20 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is chromium 33 and the bottom bar is grade 36 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 110 |
| Elongation at Break, % | 45 | |
| 11 |
| Poisson's Ratio | 0.27 | |
| 0.36 |
| Shear Modulus, GPa | 81 | |
| 39 |
| Tensile Strength: Ultimate (UTS), MPa | 850 | |
| 530 |
| Tensile Strength: Yield (Proof), MPa | 430 | |
| 520 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 370 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 420 |
| Thermal Expansion, µm/m-K | 14 | |
| 8.1 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.9 | |
| 6.3 |
| Embodied Carbon, kg CO2/kg material | 6.0 | |
| 58 |
| Embodied Energy, MJ/kg | 84 | |
| 920 |
| Embodied Water, L/kg | 250 | |
| 130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 320 | |
| 59 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 450 | |
| 1260 |
| Stiffness to Weight: Axial, points | 14 | |
| 9.3 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 30 | |
| 23 |
| Strength to Weight: Bending, points | 25 | |
| 23 |
| Thermal Shock Resistance, points | 21 | |
| 45 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0 to 0.015 | |
| 0 to 0.030 |
| Chromium (Cr), % | 31 to 35 | |
| 0 |
| Copper (Cu), % | 0.3 to 1.2 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0035 |
| Iron (Fe), % | 25.7 to 37.9 | |
| 0 to 0.030 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 |
| Molybdenum (Mo), % | 0.5 to 2.0 | |
| 0 |
| Nickel (Ni), % | 30 to 33 | |
| 0 |
| Niobium (Nb), % | 0 | |
| 42 to 47 |
| Nitrogen (N), % | 0.35 to 0.6 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.16 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 52.3 to 58 |
| Residuals, % | 0 | |
| 0 to 0.4 |