Class 1 Tungsten vs. C23000 Brass
Class 1 tungsten belongs to the otherwise unclassified metals classification, while C23000 brass belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is class 1 tungsten and the bottom bar is C23000 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 250 | |
| 110 |
| Elongation at Break, % | 5.7 | |
| 2.9 to 47 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 98 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 860 | |
| 280 to 590 |
| Tensile Strength: Yield (Proof), MPa | 580 | |
| 83 to 480 |
Thermal Properties
| Latent Heat of Fusion, J/g | 160 | |
| 190 |
| Specific Heat Capacity, J/kg-K | 120 | |
| 390 |
| Thermal Conductivity, W/m-K | 21 | |
| 160 |
| Thermal Expansion, µm/m-K | 5.1 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 12 | |
| 37 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.4 | |
| 39 |
Otherwise Unclassified Properties
| Density, g/cm3 | 15 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 22 | |
| 2.6 |
| Embodied Energy, MJ/kg | 340 | |
| 43 |
| Embodied Water, L/kg | 140 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 44 | |
| 6.2 to 260 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 660 | |
| 31 to 1040 |
| Stiffness to Weight: Axial, points | 9.6 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 14 | |
| 19 |
| Strength to Weight: Axial, points | 16 | |
| 8.9 to 19 |
| Strength to Weight: Bending, points | 14 | |
| 11 to 18 |
| Thermal Diffusivity, mm2/s | 12 | |
| 48 |
| Thermal Shock Resistance, points | 48 | |
| 9.4 to 20 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 0 | |
| 84 to 86 |
| Iron (Fe), % | 0 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Tungsten (W), % | 90 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 13.7 to 16 |
| Residuals, % | 10 | |
| 0 to 0.2 |