Class 3 Tungsten vs. C55283 Copper
Class 3 tungsten belongs to the otherwise unclassified metals classification, while C55283 copper belongs to the copper alloys. There are 15 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is class 3 tungsten and the bottom bar is C55283 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 270 | |
| 100 |
| Poisson's Ratio | 0.28 | |
| 0.34 |
| Shear Modulus, GPa | 100 | |
| 39 |
| Tensile Strength: Ultimate (UTS), MPa | 830 | |
| 190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 190 |
| Specific Heat Capacity, J/kg-K | 120 | |
| 400 |
| Thermal Expansion, µm/m-K | 4.5 | |
| 16 |
Otherwise Unclassified Properties
| Density, g/cm3 | 15 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 23 | |
| 7.9 |
| Embodied Energy, MJ/kg | 360 | |
| 120 |
Common Calculations
| Stiffness to Weight: Axial, points | 9.6 | |
| 6.8 |
| Stiffness to Weight: Bending, points | 14 | |
| 18 |
| Strength to Weight: Axial, points | 15 | |
| 6.1 |
| Strength to Weight: Bending, points | 13 | |
| 8.5 |
| Thermal Shock Resistance, points | 49 | |
| 8.0 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 0 | |
| 86.2 to 87.2 |
| Phosphorus (P), % | 0 | |
| 7.0 to 7.5 |
| Silver (Ag), % | 0 | |
| 5.8 to 6.2 |
| Tungsten (W), % | 95 | |
| 0 |
| Residuals, % | 5.0 | |
| 0 to 0.15 |