Class 4 Tungsten vs. C28000 Muntz Metal
Class 4 tungsten belongs to the otherwise unclassified metals classification, while C28000 Muntz Metal belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is class 4 tungsten and the bottom bar is C28000 Muntz Metal.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 270 | |
| 100 |
| Elongation at Break, % | 2.3 | |
| 10 to 45 |
| Poisson's Ratio | 0.28 | |
| 0.31 |
| Shear Modulus, GPa | 110 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 790 | |
| 330 to 610 |
| Tensile Strength: Yield (Proof), MPa | 580 | |
| 150 to 370 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 170 |
| Specific Heat Capacity, J/kg-K | 130 | |
| 390 |
| Thermal Conductivity, W/m-K | 30 | |
| 120 |
| Thermal Expansion, µm/m-K | 4.5 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 17 | |
| 28 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.7 | |
| 31 |
Otherwise Unclassified Properties
| Density, g/cm3 | 16 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 24 | |
| 2.7 |
| Embodied Energy, MJ/kg | 360 | |
| 46 |
| Embodied Water, L/kg | 150 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 16 | |
| 27 to 240 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 620 | |
| 110 to 670 |
| Stiffness to Weight: Axial, points | 9.6 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 14 | |
| 20 |
| Strength to Weight: Axial, points | 14 | |
| 11 to 21 |
| Strength to Weight: Bending, points | 12 | |
| 13 to 20 |
| Thermal Diffusivity, mm2/s | 15 | |
| 40 |
| Thermal Shock Resistance, points | 46 | |
| 11 to 20 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 0 | |
| 59 to 63 |
| Iron (Fe), % | 0 | |
| 0 to 0.070 |
| Lead (Pb), % | 0 | |
| 0 to 0.3 |
| Tungsten (W), % | 97 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 36.3 to 41 |
| Residuals, % | 3.0 | |
| 0 to 0.3 |