Class 4 Tungsten vs. N08800 Stainless Steel
Class 4 tungsten belongs to the otherwise unclassified metals classification, while N08800 stainless steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is class 4 tungsten and the bottom bar is N08800 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 270 | |
| 200 |
| Elongation at Break, % | 2.3 | |
| 4.5 to 34 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 110 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 790 | |
| 500 to 1000 |
| Tensile Strength: Yield (Proof), MPa | 580 | |
| 190 to 830 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 300 |
| Specific Heat Capacity, J/kg-K | 130 | |
| 480 |
| Thermal Conductivity, W/m-K | 30 | |
| 12 |
| Thermal Expansion, µm/m-K | 4.5 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 17 | |
| 1.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.7 | |
| 1.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 16 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 24 | |
| 5.3 |
| Embodied Energy, MJ/kg | 360 | |
| 76 |
| Embodied Water, L/kg | 150 | |
| 200 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 16 | |
| 42 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 620 | |
| 96 to 1740 |
| Stiffness to Weight: Axial, points | 9.6 | |
| 14 |
| Stiffness to Weight: Bending, points | 14 | |
| 24 |
| Strength to Weight: Axial, points | 14 | |
| 18 to 35 |
| Strength to Weight: Bending, points | 12 | |
| 18 to 28 |
| Thermal Diffusivity, mm2/s | 15 | |
| 3.0 |
| Thermal Shock Resistance, points | 46 | |
| 13 to 25 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0.15 to 0.6 |
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Chromium (Cr), % | 0 | |
| 19 to 23 |
| Copper (Cu), % | 0 | |
| 0 to 0.75 |
| Iron (Fe), % | 0 | |
| 39.5 to 50.7 |
| Manganese (Mn), % | 0 | |
| 0 to 1.5 |
| Nickel (Ni), % | 0 | |
| 30 to 35 |
| Phosphorus (P), % | 0 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 0.15 to 0.6 |
| Tungsten (W), % | 97 | |
| 0 |
| Residuals, % | 3.0 | |
| 0 |