Cold Drawn SAE-AISI 1108 vs. Work Hardened 90-silver 10-tin-oxide
Cold drawn SAE-AISI 1108 belongs to the iron alloys classification, while work hardened 90-silver 10-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (26, in this case) are not shown.
For each property being compared, the top bar is cold drawn SAE-AISI 1108 and the bottom bar is work hardened 90-silver 10-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 77 |
| Elongation at Break, % | 23 | |
| 7.0 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 95 | |
| 20 |
| Shear Strength, MPa | 280 | |
| 170 |
| Tensile Strength: Ultimate (UTS), MPa | 440 | |
| 300 |
| Tensile Strength: Yield (Proof), MPa | 360 | |
| 280 |