Cold Drawn SAE-AISI 1132 vs. Work Hardened 88-silver 12-tin-oxide

Cold drawn SAE-AISI 1132 belongs to the iron alloys classification, while work hardened 88-silver 12-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (26, in this case) are not shown.

For each property being compared, the top bar is cold drawn SAE-AISI 1132 and the bottom bar is work hardened 88-silver 12-tin-oxide.

Metric UnitsUS Customary Units

Material Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
84
Elongation at Break, % 14
9.0
Resilience: Ultimate (Unit Rupture Work), MJ/m3 93
24
Shear Strength, MPa 440
160
Tensile Strength: Ultimate (UTS), MPa 720
280
Tensile Strength: Yield (Proof), MPa 590
260