Cold-rolled Z21210 Zinc vs. Cold Worked Nickel 200
Cold-rolled Z21210 zinc belongs to the zinc alloys classification, while cold worked nickel 200 belongs to the nickel alloys. There are 12 material properties with values for both materials. Properties with values for just one material (21, in this case) are not shown.
For each property being compared, the top bar is cold-rolled Z21210 zinc and the bottom bar is cold worked nickel 200.
Metric UnitsUS Customary Units
Mechanical Properties
| Tensile Strength: Ultimate (UTS), MPa | 170 | |
| 540 |
Thermal Properties
| Melting Completion (Liquidus), °C | 420 | |
| 1460 |
| Melting Onset (Solidus), °C | 420 | |
| 1440 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 450 |
| Thermal Conductivity, W/m-K | 110 | |
| 69 |
| Thermal Expansion, µm/m-K | 32 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 18 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 35 | |
| 18 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.1 | |
| 8.9 |
Common Calculations
| Strength to Weight: Axial, points | 6.4 | |
| 17 |
| Strength to Weight: Bending, points | 9.4 | |
| 17 |
| Thermal Diffusivity, mm2/s | 38 | |
| 17 |