Cold-rolled Z21210 Zinc vs. Cold Worked Type 4 Magnetic Alloy
Cold-rolled Z21210 zinc belongs to the zinc alloys classification, while cold worked Type 4 magnetic alloy belongs to the nickel alloys. There are 10 material properties with values for both materials. Properties with values for just one material (22, in this case) are not shown.
For each property being compared, the top bar is cold-rolled Z21210 zinc and the bottom bar is cold worked Type 4 magnetic alloy.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 7.1 | |
| 8.8 |
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 2.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 35 | |
| 3.0 |
| Melting Completion (Liquidus), °C | 420 | |
| 1420 |
| Melting Onset (Solidus), °C | 420 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 440 |
| Strength to Weight: Axial, points | 6.4 | |
| 35 |
| Strength to Weight: Bending, points | 9.4 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 170 | |
| 1100 |
| Thermal Expansion, µm/m-K | 32 | |
| 11 |