Cold Worked R05400 Tantalum vs. Work Hardened ASTM B522 Class II
Both cold worked R05400 tantalum and work hardened ASTM B522 class II are otherwise unclassified metals. Both are furnished in the cold worked (strain hardened) condition. There are 18 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is cold worked R05400 tantalum and the bottom bar is work hardened ASTM B522 class II.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 96 |
| Elongation at Break, % | 1.1 | |
| 1.1 |
| Poisson's Ratio | 0.34 | |
| 0.41 |
| Shear Modulus, GPa | 69 | |
| 34 |
| Tensile Strength: Ultimate (UTS), MPa | 540 | |
| 490 |
| Tensile Strength: Yield (Proof), MPa | 390 | |
| 210 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 77 |
| Melting Completion (Liquidus), °C | 3020 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 140 | |
| 160 |
| Thermal Expansion, µm/m-K | 6.5 | |
| 15 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 17 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 5.5 | |
| 4.4 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 420 | |
| 230 |
| Stiffness to Weight: Axial, points | 6.2 | |
| 3.1 |
| Stiffness to Weight: Bending, points | 11 | |
| 8.9 |
| Strength to Weight: Axial, points | 9.0 | |
| 7.8 |
| Strength to Weight: Bending, points | 8.8 | |
| 8.0 |
| Thermal Shock Resistance, points | 32 | |
| 24 |
Alloy Composition
| Carbon (C), % | 0 to 0.010 | |
| 0 |
| Gold (Au), % | 0 | |
| 68.5 to 69.5 |
| Hydrogen (H), % | 0 to 0.0015 | |
| 0 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 |
| Molybdenum (Mo), % | 0 to 0.020 | |
| 0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Niobium (Nb), % | 0 to 0.1 | |
| 0 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 |
| Oxygen (O), % | 0 to 0.030 | |
| 0 |
| Platinum (Pt), % | 0 | |
| 5.5 to 6.5 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 |
| Silver (Ag), % | 0 | |
| 24.5 to 25.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Tantalum (Ta), % | 99.7 to 100 | |
| 0 |
| Titanium (Ti), % | 0 to 0.010 | |
| 0 |
| Tungsten (W), % | 0 to 0.050 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.26 |