Commercially Pure Silver vs. N06035 Nickel
Commercially pure silver belongs to the otherwise unclassified metals classification, while N06035 nickel belongs to the nickel alloys. There are 17 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is commercially pure silver and the bottom bar is N06035 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 71 | |
| 210 |
| Elongation at Break, % | 1.1 to 29 | |
| 34 |
| Poisson's Ratio | 0.37 | |
| 0.28 |
| Shear Modulus, GPa | 26 | |
| 84 |
| Shear Strength, MPa | 120 to 190 | |
| 440 |
| Tensile Strength: Ultimate (UTS), MPa | 190 to 340 | |
| 660 |
Thermal Properties
| Latent Heat of Fusion, J/g | 110 | |
| 340 |
| Melting Completion (Liquidus), °C | 960 | |
| 1440 |
| Melting Onset (Solidus), °C | 960 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 240 | |
| 450 |
| Thermal Expansion, µm/m-K | 20 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 8.4 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.8 | |
| 14 |
| Stiffness to Weight: Bending, points | 13 | |
| 24 |
| Strength to Weight: Axial, points | 4.9 to 8.9 | |
| 22 |
| Strength to Weight: Bending, points | 6.9 to 10 | |
| 20 |
| Thermal Shock Resistance, points | 9.5 to 17 | |
| 17 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.4 |
| Carbon (C), % | 0 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 32.3 to 34.3 |
| Cobalt (Co), % | 0 | |
| 0 to 1.0 |
| Copper (Cu), % | 0 | |
| 0 to 0.3 |
| Iron (Fe), % | 0 | |
| 0 to 2.0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0 | |
| 7.6 to 9.0 |
| Nickel (Ni), % | 0 | |
| 51.1 to 60.2 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0 to 0.6 |
| Silver (Ag), % | 99.9 to 100 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Tungsten (W), % | 0 | |
| 0 to 0.6 |
| Vanadium (V), % | 0 | |
| 0 to 0.2 |
| Residuals, % | 0 to 0.1 | |
| 0 |