Cordierite vs. Hexagonal Boron Nitride
Cordierite belongs to the oxide-based engineering ceramics classification, while hexagonal boron nitride belongs to the non-oxide engineering ceramics. There are 14 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is cordierite and the bottom bar is hexagonal boron nitride.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 420 | |
| 21 to 250 |
| Elastic (Young's, Tensile) Modulus, GPa | 62 | |
| 14 to 60 |
| Flexural Strength, MPa | 17 to 32 | |
| 18 to 140 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 1150 | |
| 1030 to 2350 |
| Specific Heat Capacity, J/kg-K | 800 to 850 | |
| 840 to 1610 |
| Thermal Conductivity, W/m-K | 1.3 to 1.7 | |
| 29 to 96 |
| Thermal Expansion, µm/m-K | 2.9 to 4.8 | |
| 0.54 to 18 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 4.7 | |
| 4.0 to 4.4 |
| Dielectric Strength (Breakdown Potential), kV/mm | 7.7 | |
| 61 to 200 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 9.5 | |
| 13 to 15 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.0 to 2.2 | |
| 1.9 to 2.1 |
Common Calculations
| Stiffness to Weight: Axial, points | 15 to 17 | |
| 4.1 to 18 |
| Stiffness to Weight: Bending, points | 59 to 67 | |
| 42 to 69 |
| Thermal Diffusivity, mm2/s | 0.74 to 1.0 | |
| 9.9 to 34 |